CORRO-CHEM™ 330 HHA (C)
CORRO-CHEM™ 330 HHA (C) is designed for applications where resistance to aggressive chemical exposure is of paramount importance. The sophisticated coating formula has excellent resistance to acids, acid fumes and a wide variety of solvents. Designed to be applied online up to 125°C and requires dry condition without a shutdown. Ideal for external tank, pressure vessel, piping lining, high build tank lining, pipe coating & riser protection around splash zones where application must be made to hot surfaces.
TECHNICAL DATA
- Mixing ratio 1:1 by volume
- Pot life Approx. 25 minutes at 25°C (77°F)
- Heat resistance 125°C (continuous), 149°C (intermittent)
- Dry time (to touch) 4 hours at 25°C (77°F)
- Full cure time 72 hours at 25°C (77°F)
- Salt test (ASTM D1654) 10
- Lap shear strength (ASTM D1002) 21,332 kPa
- Pull-off strength (ASTM D4541) 39,934 kPa
- Compressive strength (ASTM D695) 99,973 kPa
CORRO-HEAT 206 (C)
CORRO-HEAT 206 is formulated using a combination of liquid epoxy coating and a special high temperature curing agent. A unique feature of this combination is that although it has a high heat distortion temperature, it still cures to a hard and “dust free” condition at normal temperature. This feature is very useful since it permits convenient handling of laminates prior to final heat curing.
CORRO-DUR™ 2000 (C)
CORRO-DUR™ 2000 (C) is a 100% solids aliphatic polyamine cured solvent-free epoxy coating with solvent-free formulation optimized for application of plural component airless spray above water and by pressure pad below water. CORRO-DUR™ 2000 (C) is self-priming and functions as an anticorrosion coating by providing a tightly adherent, thick protective film. Ideal for dry or underwater online application with service in both immersed and non-immersed conditions for long-term steel protection.